Precision Ceramics Parts
-
The phase transition from γ-Al2O3 to α-Al2O3 is characterized by a reduction in surface area. Cerium oxide ceramic parts are used to prevent alpha-alumina phase transitions, helping to effectively...
-
The compressive strength is 280～500MPa. Tensile strength 25 ~ 40MPa. Bending strength 50 ~ 60MPa. The impact strength is 1.8～2.2cm·kg/cm2. Linear expansion coefficient (1.1～1.8)×10-6(20～100℃). The...
-
The ceramic plunger adopts modern engineering ceramic material with super hard wear resistance, and can be assembled and formed by ceramic metallization bonding, welding, inlay and socket...
-
SiC ceramics not only have excellent mechanical properties at room temperature, such as high flexural strength, excellent oxidation resistance, good corrosion resistance, high wear resistance and...
-
Aluminum Nitride Ceramic Parts
With a variety of modern high-precision equipment, it has independently realized the completion of the entire production process of ceramic parts from ceramic powder preparation, green body...
-
Boron Nitride Ceramic Parts have good heat resistance, thermal stability, thermal conductivity, high temperature dielectric strength, and are ideal heat dissipation materials and high temperature...
-
The phase transition from γ-Al2O3 to α-Al2O3 is characterized by a reduction in surface area. Cerium oxide ceramic parts are used to prevent alpha-alumina phase transitions, helping to effectively...
-
Tin oxide ceramic parts are ceramics with tin oxide as the main component. The flexural strength is 80MPa. Linear expansion coefficient (4.5～5)×10-6/℃. It has excellent corrosion resistance...
-
Magnesium oxide ceramics is a magnesium oxide-based material used in thick-film integrated circuits. Magnesium oxide ceramics have good conductivity, mechanical strength and high temperature...
-
Yttrium oxide ceramics, ceramics with yttrium oxide as the main crystal phase. Is a cubic crystal system. The melting point is 2430℃, the density is 5.7g/cm3, the electrical insulation is good,...
-
Titanium oxide varistor refers to a varistor ceramic material characterized by the formation of a Schottky barrier between the TiO2 grains with semiconductor properties and the grain boundary...
-
Zirconia ceramic is white, yellow or gray when it contains impurities, generally contains HfO2, and is not easy to separate. There are three crystalline states of pure ZrO2 under normal pressure....