1045 Lost Wax Investment Casting
It is mainly used to manufacture high-strength moving parts. After quenching and tempering, the parts have good comprehensive mechanical properties.
Product Introduction
|
1045 lost wax investment casting |
|||||||
|
Item |
Material |
Production Process |
Sintering Temperature |
Mold |
Custom |
||
|
1045 lost wax investment casting |
1045 |
Molten mold casting |
1380℃ |
To be customized |
Yes |
||
|
Chemical composition |
C：0.43~0.50% Si：0.10~0.40% Mn：0.60~0.90% P： 0.040% S： 0.050% |
||||||
|
Available Materials |
Carbon steel, alloy steel, aluminum alloy, low -carbon stainless steel, titanium alloy (TI, TC4), copper alloy, high temperature alloy (718, 713) |
||||||
|
Smoothness |
Dimensional accuracy |
Product density |
Appearance treatment |
Appropriate weight |
|||
|
Roughness 1～5μm |
(±0.1%～±0.5%) |
7.8g/CM³ |
According to customer requirements |
3g～4kg) |
|||
Mechanical Properties of 1045 Carbon Steel
Density (kg/m3): about 7850
Tensile strength b(MPa): 600
Yield strength s(MPa): 355
Elongation 5(%): 16
Reduction of area (%): 40
Impact power Akv(J): 39
Brinell hardness (HBS10/3000) (annealed state): ≦197
Brinell hardness (HBS10/3000) (hot rolled state): ≦229
Sample size: The sample blank size is 25mm
Scope of Application of 1045 Carbon Steel
It is mainly used to manufacture high-strength moving parts. After quenching and tempering, the parts have good comprehensive mechanical properties. 1045 lost wax investment casting is widely used in various important structural parts, such as turbine impellers, compressor pistons, shafts, and gears. , racks, worms, crankshaft spindles, drive shafts, piston rods, connecting rods, chain rods, etc. If the parts are required to have high hardness and high wear resistance, quenching and tempering + surface quenching can be used to increase the surface hardness.
Micro Structure
Heat treatment specifications: normalizing, 850℃; quenching, 840℃; tempering, 600℃.
Delivery Status
Delivered in unheated or heat treated (annealed, normalized, or high temperature tempered) state. If the product is required to be delivered in a heat-treated state, it should be stated in the contract. If it is not stated, it will be delivered without heat treatment.