1046 Lost Wax Investment Casting
1046 lost wax investment casting is widely used in various important structural parts, such as turbine impellers, compressor pistons, shafts, and gears, racks, worms, crankshaft spindles, drive shafts, piston rods, connecting rods, chain rods, etc.
Product Introduction
|
1046 lost wax investment casting |
|||||||
|
Item |
Material |
Production Process |
Sintering Temperature |
Mold |
Custom |
||
|
1046 lost wax investment casting |
1046 |
Molten mold casting |
1380℃ |
To be customized |
Yes |
||
|
Chemical composition |
C ：0.42～0.50% Si：0.17～0.37% Mn：0.70～1.00% S ：≤0.035% P ：≤0.035% Cr：≤0.25% Ni：≤0.25% Cu：≤0.25% |
||||||
|
Available Materials |
Carbon steel, alloy steel, aluminum alloy, low -carbon stainless steel, titanium alloy (TI, TC4), copper alloy, high temperature alloy (718, 713) |
||||||
|
Smoothness |
Dimensional accuracy |
Product density |
Appearance treatment |
Appropriate weight |
|||
|
Roughness 1～5μm |
(±0.1%～±0.5%) |
7.8g/CM³ |
According to customer requirements |
3g～4kg) |
|||
1046 is high quality carbon structural steel
Corresponding brand
National standard brand 45Mn
Japanese brand number SWRCH45K
American Standard No. 1046
German brand number C45EC
Mechanical Properties of 1046 Carbon Steel
Density ρ (kg/m3): about 7850
Tensile strength σb (MPa): ≥600
Yield strength σs (MPa): ≥355
Elongation δ5(%): ≥16
Area shrinkage ψ(%): ≥40
Impact power Akv(J): ≥39
Brinell hardness (HBS10/3000) (annealed state): ≦197
Brinell hardness (HBS10/3000) (hot rolled state): ≦229
Sample size: The sample blank size is 25mm
Scope of Application of 1046 Carbon Steel
It is mainly used to manufacture high-strength moving parts. After quenching and tempering, the parts have good comprehensive mechanical properties. 1046 lost wax investment casting is widely used in various important structural parts, such as turbine impellers, compressor pistons, shafts, and gears, racks, worms, crankshaft spindles, drive shafts, piston rods, connecting rods, chain rods, etc. If the parts are required to have high hardness and high wear resistance, quenching and tempering + surface quenching can be used to increase the surface hardness.