XC38TS Lost Wax Investment Casting
XC38TS lost wax investment casting is widely used in manufacturing various forgings and lost wax investment castings, cold drawn and upset steel materials, seamless steel pipes, parts in machinery manufacturing, such as crankshafts, rotating shafts, pins, levers, connecting rods, beams, sleeves, rims, washers, screws, nuts, motorcycle frames, etc.
Product Introduction
|
XC38TS lost wax investment casting |
|||||||
|
Item |
Material |
Production Process |
Sintering Temperature |
Mold |
Custom |
||
|
XC38TS lost wax investment casting |
XC38TS |
Molten mold casting |
1380℃ |
To be customized |
Yes |
||
|
Chemical composition |
C ：0.32～0.40 Si：0.17～0.37 Mn：0.50～0.80 S ：≤0.035 P ：≤0.035 Cr：≤0.25 Ni：≤0.25 Cu：≤0.25 |
||||||
|
Available Materials |
Carbon steel, alloy steel, aluminum alloy, low -carbon stainless steel, titanium alloy (TI, TC4), copper alloy, high temperature alloy (718, 713) |
||||||
|
Smoothness |
Dimensional accuracy |
Product density |
Appearance treatment |
Appropriate weight |
|||
|
Roughness 1～5μm |
(±0.1%～±0.5%) |
7.8g/CM³ |
According to customer requirements |
3g～4kg) |
|||
Mechanical Properties
Tensile strength σb (MPa): ≥530(54)
Yield strength σs (MPa): ≥315(32)
Elongation δ5 (%): ≥20
Reduction of area ψ (%): ≥45
Impact energy Akv (J): ≥55
Impact toughness value αkv (J/cm²): ≥69(7)
Hardness: not heat treated ≤197HB
Sample size: The sample size is 25mm
Application
XC38TS lost wax investment casting is widely used in manufacturing various forgings and lost wax investment castings, cold drawn and upset steel materials, seamless steel pipes, parts in machinery manufacturing, such as crankshafts, rotating shafts, pins, levers, connecting rods, beams, sleeves, rims, washers, screws, nuts, motorcycle frames, etc.
Heat treatment specifications and metallographic structure:
Heat treatment specifications: normalizing, 870℃; quenching, 850℃; tempering, 600℃.
Metallographic structure: ferrite + pearlite.
Delivery status: Delivery without heat treatment or heat treatment (annealing, normalizing, or high-temperature tempering). If the product is required to be delivered in a heat-treated state, it should be stated in the contract. If it is not stated, it will be delivered without heat treatment.