4142 Lost Wax Investment Casting
4142 alloy steel is a medium carbon alloy steel whose main components are carbon, chromium, molybdenum, and manganese. It has the characteristics of high strength, wear resistance, corrosion resistance, and weldability, and can be used to manufacture high-quality industrial equipment.
Product Introduction
|
4142 lost wax investment casting |
|||||||
|
Item |
Material |
Production Process |
Sintering Temperature |
Mold |
Custom |
||
|
4142 lost wax investment casting |
4142 lost wax investment casting |
Molten mold casting |
1380℃ |
To be customized |
Yes |
||
|
Chemical composition |
(C): 0.40-0.45% (Cr): 0.80-1.10% (Mo): 0.15-0.25% (Mn): 0.75-1.00% (Si): 0.15-0.35% (P): 0.035% or less (S): 0.040% or less |
||||||
|
Available Materials |
Carbon steel, alloy steel, aluminum alloy, low -carbon stainless steel, titanium alloy (TI, TC4), copper alloy, high temperature alloy (718, 713) |
||||||
|
Smoothness |
Dimensional accuracy |
Product density |
Appearance treatment |
Appropriate weight |
|||
|
Roughness 1～5μm |
(±0.1%～±0.5%) |
7.8g/CM³ |
According to customer requirements |
3g～4kg) |
|||
4142 alloy steel is a medium carbon alloy steel whose main components are carbon, chromium, molybdenum, and manganese. It has the characteristics of high strength, wear resistance, corrosion resistance, and weldability, and can be used to manufacture high-quality industrial equipment such as aircraft, cars, rockets, and motorcycles.
These elements work together to give 4142 alloy steel the corresponding physical and mechanical properties.
The heat treatment characteristics of 4142 alloy steel are also very important. Typically, heat treatment increases hardness and strength and improves wear and corrosion resistance.
The specific heat treatment methods are:
1. Solution treatment: Dissolve 4142 alloy steel at high temperature to completely dissolve it. It is then rapidly cooled in water to form a uniform grain structure.
2. Cooling and quenching treatment: heat 4142 alloy steel to the appropriate temperature and then quench in water. This treatment hardens the steel and increases its strength and wear resistance.
3. High-temperature quenching treatment: Heat the 4142 alloy steel to an appropriate temperature and keep it warm for a period of time to heat it evenly. Then it is cooled at an appropriate speed to achieve the effect of optimizing various physical and mechanical properties.
In general, 4142 lost wax investment casting has high mechanical properties and heat treatment properties and is a high-strength, high-durability steel.