N20H20 Metal Powder Injection Molded Parts
Rapid annealing: heating temperature is 350-410°C; depending on the effective thickness of the material, the holding time is between 30-120min; air or water cooling. 2 High-temperature annealing: heating temperature 350-500 ℃; when the thickness of the finished product is ≥ 6mm, the holding time is 10-30min, and when it is less than 6mm, it is until the heat penetrates; air cooling. 3 Low-temperature annealing: heating temperature 150-250 ℃; holding time 2-3 hours; air or water cooling. Homogenization: 570 degrees Celsius, heat preservation for 7 hours, air cooling.
Product Description
|
N20H20 metal powder injection molded parts |
|||||
|
Item |
Material |
Production Process |
Sintering Temperature |
Mold |
Custom |
|
N20H20 |
Aluminum alloy |
Metal Injection Molding |
1500°C |
To be customized |
Yes |
|
Chemical composition |
unit:% Cu:0.15～0.4 Mn :0.15 Mg :0.8～1.2 Zn :0.25 Cr:0.04～0.35 Ti :0.15 Si:0.4～0.8 Fe :≤0.7 Al : Margin |
||||
|
Available Materials |
Low carbon stainless steel, titanium alloy (Ti, TC4), copper alloy, tungsten alloy, hard alloy, high temperature alloy (718, 713) |
||||
N20H20 mechanical properties
The ultimate tensile strength of 6061 is above 205 MPa
Compressive yield strength 55.2 MPa
Elastic coefficient 68.9 GPa
Bending ultimate strength 228 MPa
Bending Yield Strength 103 MPa
N20H20 heat treatment
Rapid annealing: heating temperature is 350-410°C; depending on the effective thickness of the material, the holding time is between 30-120min; air or water cooling. 2 High-temperature annealing: heating temperature 350-500 ℃; when the thickness of the finished product is ≥ 6mm, the holding time is 10-30min, and when it is less than 6mm, it is until the heat penetrates; air cooling. 3 Low-temperature annealing: heating temperature 150-250 ℃; holding time 2-3 hours; air or water cooling. Homogenization: 570 degrees Celsius, heat preservation for 7 hours, air cooling.
A warm reminder to you that the density of 6061 aluminum alloy is 2800kg/m^3
N20H20 corresponding grade
National Standard: 6061 LD30 GB/T 3190-2008
ISO: AlMg1SiCu ISO 209.1-1989
Japanese standard: A6061 JIS H4000-1999 JIS H4040-1999
Non-standard: 65032 IS 733-2001 IS 737-2001
EN:EN AW-6061/AlMg1SiCu EN 573-3-1994
German standard: AlMgSi1Cu/3.3211 DIN 1725.1-1986/W-Nr
French standard: 6061 A-GSUC NF A50-411 NF A50-451
British Standard: 6061 N20/H20 BS 1470-1988
American Standard: 6061/A96061 AA/UNS
Metal Injection Molding Process
Detection Systems
Send Inquiry